Characterization of sintered Ag nanopowder joints using nanoindentation tests

Varování

Publikace nespadá pod Ekonomicko-správní fakultu, ale pod Přírodovědeckou fakultu. Oficiální stránka publikace je na webu muni.cz.

Autoři	BURŠÍK Jiří SOPOUŠEK Jiří BURŠÍKOVÁ Vilma STÝSKALÍK Aleš ŠKODA David
Rok publikování	2011
Druh	Článek v odborném periodiku
Časopis / Zdroj	Chem. listy
Fakulta / Pracoviště MU	Přírodovědecká fakulta
Citace
Obor	Fyzika plazmatu a výboje v plynech
Klíčová slova	Nanoindentation; Silver nanopowder; Solder
Popis	Sandwiches consisting of copper disks with Ag nanopowder interlayer annealed at various temperatures from 200 to 350 C were studied. The main emphasis was placed on the characterization of quality of the sintered Ag layers by means of nanoindentation experiments. The highest hardness values were obtained after annealing at 350 C. The highest values of the Young's modulus were achieved after annealing at 250 C, indicating the lowest porosity of the sintered layer.