Structural and magnetic properties of Fe-oxide layers prepared by inkjet printing on Si-substrate

Varování

Publikace nespadá pod Ekonomicko-správní fakultu, ale pod Přírodovědeckou fakultu. Oficiální stránka publikace je na webu muni.cz.
Autoři

ZAŽÍMAL František SVOBODA Tomáš DZIK Petr HOMOLA Tomáš JIRÁSKOVÁ Yvonna

Rok publikování 2021
Druh Článek ve sborníku
Konference NANOCON 2020: 12th International Conference on Nanomaterials - Research & Application
Fakulta / Pracoviště MU

Přírodovědecká fakulta

Citace
www https://doi.org/10.37904/nanocon.2020.3682
Doi http://dx.doi.org/10.37904/nanocon.2020.3682
Klíčová slova Inkjet printing; hematite; physical properties; testing methods
Popis Magnetic films with two, four, six, and eight layers were prepared using 2D inkjet printing on the 333 K heated Si-substrates at ambient conditions. The microstructure, phase composition of layers, and magnetic studies were investigated using wide spectrum of experimental methods with the aim to find the optimal conditions for producing magnetic sensors by digital printing technology in the near future. As the magnetic compound, the hematite powder was chosen and its milling with Si-binder dissolved in dowanol using glass balls and vial to prevent contamination was done to prepared suspension appropriate for printing. It is shown that hematite transformed markedly into maghemite, thus the layers consisted of small amount hematite and dominant maghemite phases determining the magnetic properties. From the viewpoint of magnetic behavior, the highest saturation magnetization and the lowest coercivity was obtained at the sample with 8 layers.