Solvothermal hot injection metal nanoalloy synthesis

Logo poskytovatele
Logo poskytovatele

Varování

Publikace nespadá pod Ekonomicko-správní fakultu, ale pod Přírodovědeckou fakultu. Oficiální stránka publikace je na webu muni.cz.
Název česky Solvotermální syntéza kovových nanoslitin připravených vstřikováním za horka
Autoři

VYKOUKAL Vít PINKAS Jiří

Rok publikování 2016
Druh Další prezentace na konferencích
Fakulta / Pracoviště MU

Přírodovědecká fakulta

Citace
Přiložené soubory
Popis Nanomaterials and especially their preparation by chemical approach is a very active field of materials research. The synthesis of nanoalloys is one integral part of nanoscience and development of efficient methods is a challenging task due to their chemical, phase, and morphological variability. Nanoparticles of metal alloys exhibit many interesting properties, such as depression of melting point, plasmon resonance, catalytic activity5 and phase separation. Nanoalloys can be prepared by many approaches, but the solvothermal synthesis, specifically in oleylamine is highly advantageous. Hot injection technique should ensure homogeneous conditions for nanoparticles nucleation and growth. AgNi nanoparticles were prepared by injection of an oleylamine solution (4 cm3) of AgNO3 and Ni(acac)2 (different molar ratios, 4 mmol total amount) to a mixture of oleylamine (16 cm3) and octadecene (20 cm3) at 230 °C. After 10 minutes, the reaction mixture was cooled down to room temperature in a water bath. Then 20 cm3 of acetone was added to precipitate nanoparticles and the suspension was centrifuged. The precipitate was washed by a mixture of hexane and acetone (1:3 volume ratio). This procedure was repeated twice and finally the precipitate was dispersed in hexane and characterized. Dynamic Light Scattering (DLS), Transmission Electron Microscopy (TEM), Elemental analyses (ICP OES), and Small-Angle X-ray Scattering (SAXS) analyses were performed for determination of chemical composition, average size, size distribution, and shape of the prepared nanoparticles. Plasmon resonances were also observed. Phase separation was observed by High Temperature X-Ray Diffraction (HT-XRD) technique and was confirmed by Scanning Electron Microscope (SEM) and by measuring of magnetic properties during heating.
Související projekty:

Používáte starou verzi internetového prohlížeče. Doporučujeme aktualizovat Váš prohlížeč na nejnovější verzi.