Comparison of nc-TiC/a-C:H nanocomposite coatings deposited by DC magnetron sputtering at low and high flux of impinging ions

Logo poskytovatele
Logo poskytovatele

Varování

Publikace nespadá pod Ekonomicko-správní fakultu, ale pod Přírodovědeckou fakultu. Oficiální stránka publikace je na webu muni.cz.
Autoři

SOUČEK Pavel SCHMIDTOVÁ Tereza ZÁBRANSKÝ Lukáš BURŠÍKOVÁ Vilma VAŠINA Petr CAHA Ondřej BURŠÍK Jiří PEŘINA Vratislav PEI Yutao DE HOSSON J.Th.M.

Rok publikování 2013
Druh Konferenční abstrakty
Fakulta / Pracoviště MU

Přírodovědecká fakulta

Citace
Popis Nanocrystalline titanium carbide embedded in an amorphous (hydrogenated) carbon matrix, is a versatile nanocomposite material combining properties of hard titanium carbide grains and a soft carbon matrix. Depending on the content of the TiC phase and a-C(:H) phase the properties can be tailored from very hard films with hardness reaching over 40 GPa and Young’s modulus higher than 300 GPa respectively to low friction films with friction coefficient around 0.1 and low wear rate. Magnetron sputtering of titanium target in acetylene containing atmosphere is the most used method of nc-TiC/a-C(:H) coatings preparation. In this research, role of energetic ion bombardment on the coating quality was studied in details. A well-balanced magnetic field configuration leading to saturated ion current on the substrate of ~0.3 mA/cm2 and strongly unbalanced magnetic field ~2 mA/cm2 was used. Structure, mechanical and tribological properties of the resulting 4-6 micrometers thick well adherent coatings deposited on high speed steel and cemented tungsten carbide substrates was analyzed and compared. The structure, mechanical and tribological parameters were found to be strongly dependent on the chemical composition of the rating, though nearly independent on the impinging ion flux on the substrate