Laser ablation synthesis of new gold tellurides using tellurium and nanogold as precursors. Laser desorption ionisation time-of-flight mass spectrometry

Logo poskytovatele

Varování

Publikace nespadá pod Ekonomicko-správní fakultu, ale pod Přírodovědeckou fakultu. Oficiální stránka publikace je na webu muni.cz.
Autoři

ŠVIHLOVÁ Katarína PROKEŠ Lubomír SKÁCELOVÁ Dana PEŇA MÉNDEZ Eladia Maria HAVEL Josef

Rok publikování 2013
Druh Článek v odborném periodiku
Časopis / Zdroj Rapid Commun. Mass Spectrom
Fakulta / Pracoviště MU

Přírodovědecká fakulta

Citace
www http://onlinelibrary.wiley.com/doi/10.1002/rcm.6613/pdf
Doi http://dx.doi.org/10.1002/rcm.6613
Obor Analytická chemie, separace
Klíčová slova Laser Desorption Ionisation (LDI); nanogold-Te; DCSBD
Popis RATIONALE: Only a few gold tellurides are known. However, Laser Ablation Synthesis (LAS) using Laser Desorption Ionisation (LDI) time-of-flight mass spectrometry (TOF MS) has high potential for the generation of new compounds. METHODS: LDI of nanogold-Te conjugate using a nitrogen laser 337 nm was applied while the mass spectra were recorded in positive and negative ion modes using a quadrupole ion trap-TOF mass spectrometer equipped with a reflectron. Diffuse coplanar surface barrier discharge was applied for the plasma treatment of glass and silicon surfaces. RESULTS: A form of nanogold-Te conjugate was prepared and found suitable for LAS of gold tellurides. Several new AumTen (m=1–11; n=1–4) clusters were identified. An excess of nanogold and chloride or an excess of auric acid caused the formation of mixed AumTenClx clusters. The nanogold-Te conjugate can be deposited from an aqueous suspension onto glass while the deposition is strongly enhanced if the surface is modified by plasma. CONCLUSIONS: LDI of nanogold-Te conjugate is a suitable procedure for the generation of new gold telluride clusters. Treatment of borosilicate glass with a diffuse coplanar surface barrier discharge strongly enhances the deposition of gold tellurides on glass while limited adsorption on a silicon surface was observed.